Corrosion behavior and characteristics of the product film of API X100 steel in acidic simulated soil solution

[PDF]

Corrosion behavior and characteristics of the product film

C.W. Du et al., Corrosion behavior and characteristics of the product film of API X100 steel in acidic simulated soil … 177 or near- neutral pH solutions. Research into the corrosion of X100 in acidic simulated soil solution has not been reported.

Corrosion behavior and characteristics of the product film

The short-term corrosion behavior of API X100 steel in an acidic simulated soil was investigated by electrochemical measurements and soaking experiments, followed by corrosion morphology observations and X-ray photoelectron spectroscopy analyses.

(PDF) Corrosion behavior and characteristics of the

The short-term corrosion behavior of API X100 steel in an acidic simulated soil was investigated by electrochemical measurements and soaking experiments, followed by corrosion morphology

Corrosion behavior and characteristics of the product film

The short-term corrosion behavior of API X100 steel in an acidic simulated soil was investigated by electrochemical measurements and soaking experiments, followed by corrosion morphology observations and X-ray photoelectron spectroscopy analyses.

Influence of temperature on the corrosion behavior of API

The short-term corrosion behavior of API X100 steel in an acidic simulated soil was investigated by electrochemical measurements and soaking experiments, followed by corrosion morphology

An Electrochemical Model for Prediction of Corrosion of

(2016) Corrosion behavior and characteristics of the product film of API X100 steel in acidic simulated soil solution. International Journal of Minerals, Metallurgy, and Materials 23:2, 176-183. Online publication date: 31-Jan-2016.

Corrosion behavior of API X100 steel in near-neutral pH

Corrosion behavior of API X100 steel in near-neutral pH bicarbonate environments: experimental and modelling studies by IBRAHIM M. GADALA B.A.Sc. with distinction, The University of …

Electrochemical behavior of API-X100 pipeline steel in NS4

API X-100 pipeline steel specimens were subject to a matrix of environmental conditions characterized by bicarbonate content, purging gas, solution temperature, chloride and/or sulfate ions, and resultant solution …

[PDF]

Low Alloy X100 Pipeline Steel Corrosion and Passivation

Solutions of pH 6.7 to 8.9 with Groundwater Anions: An Electrochemical Study IBRAHIM M. GADALA and AKRAM ALFANTAZI This research investigates the fundamental corrosion and passivation processes occurring on API-X100 pipeline steels before, during, and after passive layer formation in bicarbonate-based simulated soil solutions of pH 6.7 to 8.9.

Electrochemical evaluation of the corrosion behaviour of

This work is devoted to evaluating electrochemical corrosion aspects of API-X100 in bicarbonate solutions. They were prepared to be aerated; chloride free and 3 wt.% chloride containing solutions of 0.1, 0.5, and 0.8 M bicarbonate at 20, 40, and 60 °C.Open circuit potentials, polarization potentiodynamics, and impedance spectroscopy were utilized.

The stress corrosion cracking behavior of X120 pipeline

4.1 Corrosion behavior of X120 steel in simulated acidic soil solution. The anodic reaction of X120 steel in deaerated acidic soil solution is primarily oxidation of iron: Equation 2 The cathodic process may include several reactions.

Published in: Anti-corrosion Methods and Materials · 2012Authors: Jing Liu · Jihao Cheng · Qian Hu · Feng Huang · Jinqiao Xu · Bin GuoAffiliation: Wuhan University of Science and TechnologyAbout: Pipeline transport · Stress corrosion cracking · Hydrogen embrittlement · Corrosion

Characteristics of Corrosion Scales on Steels in a CO 2

(2019) A comparative study on the corrosion behaviors of X100 steel in simulated oilfield brines under the static and dynamic conditions. Journal of Petroleum Science and Engineering 173, 1109-1120. Online publication date: 1-Feb-2019.

Published in: Corrosion · 1991Authors: Carlos A Palacios · J R ShadleyAffiliation: University of TulsaAbout: Sodium · Chemical reaction · Drilling fluid · Corrosion · Natural gas · Surface layer

Corrosion behavior of API 5L X‐60 pipeline steel exposed

Soil parameters influence on pipeline steel corrosion behaviour exposed in near‐neutral pH soil simulating solution has been investigated by potentiodynamic polarisation and EIS method. Results showed that the steel corrosion increases, corrosion current density increases with temperature in the range from 20 to 60 °C.

Corrosion Behavior of API X100 Steel Material in A

TheThephenomenon phenomenon ofofthetheformation formationof a of sulfide film and a sulfide its and film cracking is its cracking is influenced by test solution conditions [47].2 S. (d) 21 ppm. images SEM imagesof API X100 of API steel X100 material steel materialfor …